PRODUCT INTRODUCTIONS
CM6050 is used for wire and cables,and hoses industries,not containing wax,good resistance to tearing and friction,and very good mechanical property.
SPECIFICATIONS
Rubber specifications before vulcanization |
Specifications |
CM6050 |
Chlorine content,% |
36±1 |
Heat of fusion,Jg |
≤1.5 |
Volatile matter,% |
≤0.3 |
Impurity particles unit/200g |
≤40 |
Shore A hardness |
≤55 |
Tensile strength Mpa |
≥8 |
Elongation at break,% |
≥700 |
Mooney viscosity ML(1+4)125ºC |
55±5 |
Ash content,% |
≤4.5 |
Rubber specifications before vulcanization |
Vulcanization conditions |
170ºC,10min |
Shore A hardness |
75 |
100% strain Mpa |
4.6 |
Tensile strength Mpa |
14.0 |
Elongation at break % |
393 |
Mooney viscosity ML(1+4)100C |
59 |
APPLICATIONS
CM6050 is a kind of chlorinated polyethylene with low Mooney viscosity and high volume resistivity,it is suitable for cables,wires and rubber hoses,with very good products appearance and high extruding speed;It is also suitable for magnetic materials,with very good soft property and processing property at low temperature,and high filling capacity for magnetic powder.
Product details
R&D TEAM
Packing
25 kg PP woven bag or 500 kg / 550 kg supre sacks.
Transportation
This material is non - dangerous goods for land, air and marine transportation.
Storage
To avoid blocking, bags should be stored in the dry and ventilated warehouse with stack height no more than 10 bags and avoid solarization, damp and takes strict precautions again stress. shelf life is theoretically unlimited when storage is under proper conditions.
Factory